Bitumen 40-50
Bitumen 40-50 is which is obtained by performing aeration process on vacuum baton (raw material of bitumen production which is taken from the bottom of distillation tower in the vacuum of oil refineries) in bitumen production units so that its permeability is between 40 Up to 50. Used in road construction industries for tropical areas, insulation and also the production of liquid bitumen is one of the applications of this type of bitumen
| Analysis Of Bitumen 40/50 | ||||
| SPECIFICATION | Unti | Limit | TEST METHOD | |
| DENSITY @ 25 C | kg/m3 | 1010-1060 | ASTM D70 or D3289 | |
| PENETRATION @ 25 C | Mm/10 | 40-50 | ASTM D5 | |
| SOFTENING POINT | C | 49 min | ASTM D36 | |
| DUCTILITY@ 25 C | Cm | 100 min | ASTM D 113 | |
| LOSS ON HEATING | wt% | 0.2 max | ASTM D6 | |
| DROP IN PENETERATION AFTER LOSS ON HEATING | % | 20 max | ASTM D5 | |
| FLASH POINT | C | 232 min | ASTM D92 | |
| SOLUBILITY IN TRICHLOROETHYLENE | wt% | 99.0 min | ASTM D2042 | |
| SPOT TEST | – | Negative | AASHTO T 102 | |
| VISCOSITY @ 60C | P | 4000±800 | ASTM D2171 | |
| VISCOSITY @ 135C | Cst | 400 min | ASTM D1270 | |
| Test on Residue From Thin Film Oven Test (ASTM D1754) | ||||
| Retained penetration after (T.F.O.T) | % | 58 min | ASTM D5 | |
| Ductility . (25C), 5cm/min, cm after TFOT | cm | 50 | ASTM D113 | |
| VISCOSITY @ 60C | P | 20000 max | ASTM D2171 | |
BITUMEN 60-70
Road bitumens are classified based on the results of penetration degree and soft spot tests. The classification is based only on the penetration range, for example, bitumen 60-70 has a penetration degree between 70 and 60 and a softening point between 48 and 52 oC. The main part of penetrating bitumens 60-70 bitumen which is used in road construction.
| Analysis Of Bitumen 60/70 | ||||
| SPECIFICATION | Unti | Limit | TEST METHOD | |
| DENSITY @ 25 C | kg/m3 | 1010-1060 | ASTM D70 or D3289 | |
| PENETRATION @ 25 C | Mm/10 | 60-70 | ASTM D5 | |
| SOFTENING POINT | C | 49 min | ASTM D36 | |
| DUCTILITY@ 25 C | Cm | 100 min | ASTM D 113 | |
| LOSS ON HEATING | wt% | 0.2 max | ASTM D6 | |
| DROP IN PENETERATION AFTER LOSS ON HEATING | % | 20 max | ASTM D5 | |
| FLASH POINT | C | 232 min | ASTM D92 | |
| SOLUBILITY IN TRICHLOROETHYLENE | wt% | 99.0 min | ASTM D2042 | |
| SPOT TEST | – | Negative | AASHTO T 102 | |
| VISCOSITY @ 60C | P | 2000±400 | ASTM D2171 | |
| VISCOSITY @ 135C | Cst | 300 min | ASTM D1270 | |
| Test on Residue From Thin Film Oven Test (ASTM D1754) | ||||
| Retained penetration after (T.F.O.T) | % | 54 min | ASTM D5 | |
| Ductility . (25C), 5cm/min, cm after TFOT | cm | 50 | ASTM D113 | |
| VISCOSITY @ 60C | P | 10000 max | ASTM D2171 | |
BITUMEN 85-100
One of the products of Vectal Oil Company is bitumen with a degree of penetration (bitumen hardness) of 85-100. bitumen which is obtained by performing aeration process on vacuum baton (raw material of bitumen production which is taken from the residue of distillation tower in the vacuum of oil refineries) in bitumen production units. The most common use of bitumen is in road construction, insulation, construction, and also the production of liquid bitumen. This product is more suitable for cold regions of the country in terms of place of use. Vectal Oil Company has been able to take a big step in introducing high-quality Iranian bitumen by producing bitumen, 85-100 bitumen packaging, and exporting bitumen to more than 40 countries
| Analysis Of Bitumen 85/100 | ||||
| SPECIFICATION | Unti | Limit | TEST METHOD | |
| DENSITY @ 25 C | kg/m3 | 1000-1050 | ASTM D70 or D3289 | |
| PENETRATION @ 25 C | Mm/10 | 85-100 | ASTM D5 | |
| SOFTENING POINT | C | 42 min | ASTM D36 | |
| DUCTILITY@ 25 C | Cm | 100 min | ASTM D 113 | |
| LOSS ON HEATING | wt% | 0.5 max | ASTM D6 | |
| DROP IN PENETERATION AFTER LOSS ON HEATING | % | 20 max | ASTM D5 | |
| FLASH POINT | C | 232 min | ASTM D92 | |
| SOLUBILITY IN TRICHLOROETHYLENE | wt% | 99.0 min | ASTM D2042 | |
| SPOT TEST | – | Negative | AASHTO T 102 | |
| VISCOSITY @ 60C | P | 1000±200 | ASTM D2171 | |
| VISCOSITY @ 135C | Cst | 250 min | ASTM D1270 | |
| Test on Residue From Thin Film Oven Test (ASTM D1754) | ||||
| Retained penetration after (T.F.O.T) | % | 50 min | ASTM D5 | |
| Ductility . (25C), 5cm/min, cm after TFOT | cm | 75 | ASTM D113 | |
| VISCOSITY @ 60C | P | 5000 max | ASTM D2171 | |
Bitumen 120-150
Bitumen 120-150, which is obtained by performing the aeration process on vacuum baton (raw material for bitumen production, which is taken from the bottom of the distillation tower in the vacuum of oil refineries) in bitumen production units and the degree of permeability (determination of stiffness). Bitumen) it should be between 120 and 150. The main common use of this product is in very cold and icy areas
| Analysis Of Bitumen 120/150 | ||||
| SPECIFICATION | Unti | Limit | TEST METHOD | |
| DENSITY @ 25 C | kg/m3 | 1000-1050 | ASTM D70 or D3289 | |
| PENETRATION @ 25 C | Mm/10 | 120-150 | ASTM D5 | |
| SOFTENING POINT | C | 38 min | ASTM D36 | |
| DUCTILITY@ 25 C | Cm | 100 min | ASTM D 113 | |
| LOSS ON HEATING | wt% | 0.5 max | ASTM D6 | |
| DROP IN PENETERATION AFTER LOSS ON HEATING | % | 20 max | ASTM D5 | |
| FLASH POINT | C | 218 min | ASTM D92 | |
| SOLUBILITY IN TRICHLOROETHYLENE | wt% | 99.0 min | ASTM D2042 | |
| SPOT TEST | – | Negative | AASHTO T 102 | |
| VISCOSITY @ 60C | P | 450±90 | ASTM D2171 | |
| VISCOSITY @ 135C | Cst | 170 min | ASTM D1270 | |
| Test on Residue From Thin Film Oven Test (ASTM D1754) | ||||
| Retained penetration after (T.F.O.T) | % | 46 min | ASTM D5 | |
| Ductility . (25C), 5cm/min, cm after TFOT | cm | 100 | ASTM D113 | |
| VISCOSITY @ 60C | P | 2250 max | ASTM D2171 | |
Bitumen 150-200
Bitumen Penetration Grade 100/150 is a standard penetration grade Bitumen usually used as a Paving Grade Bitumen suitable for road construction and for the production of asphalt pavements with superior properties. This grade of Bitumen is mainly used in the manufacture of hot mix asphalt for bases and wearing courses. Bitumen 100/150 is suitable for road construction and for the asphalt pavements with superior properties. This type of bitumen used in the manufacture of hot mix asphalt for bases and wearing courses.
| Analysis Of Bitumen 150-200 | ||||
| SPECIFICATION | Unti | Limit | TEST METHOD | |
| DENSITY @ 25 C | kg/m3 | 1000-1050 | ASTM D70 or D3289 | |
| PENETRATION @ 25 C | Mm/10 | 150-200 | ASTM D5 | |
| SOFTENING POINT | C | 36 min | ASTM D36 | |
| DUCTILITY@ 25 C | Cm | 100 min | ASTM D 113 | |
| LOSS ON HEATING | wt% | 0.5 max | ASTM D6 | |
| DROP IN PENETERATION AFTER LOSS ON HEATING | % | 20 max | ASTM D5 | |
| FLASH POINT | C | 218 min | ASTM D92 | |
| SOLUBILITY IN TRICHLOROETHYLENE | wt% | 99.0 min | ASTM D2042 | |
| SPOT TEST | – | Negative | AASHTO T 102 | |
| VISCOSITY @ 60C | P | 250±50 | ASTM D2171 | |
| VISCOSITY @ 135C | Cst | 150 min | ASTM D1270 | |
| Test on Residue From Thin Film Oven Test (ASTM D1754) | ||||
| Retained penetration after (T.F.O.T) | % | 46 min | ASTM D5 | |
| Ductility . (25C), 5cm/min, cm after TFOT | cm | 100 | ASTM D113 | |
| VISCOSITY @ 60C | P | ASTM D2171 | ||
Bitumen 200-300
Bitumen Penetration Grade 200/300 is a standard penetration grade Bitumen usually used as a Paving Grade Bitumen suitable for road construction and for the production of asphalt pavements with superior properties. This grade of Bitumen is mainly used in the manufacture of hot mix asphalt for bases and wearing courses. Bitumen 200/300 is suitable for road construction and for the asphalt pavements with superior properties. This type of bitumen used in the manufacture of hot mix asphalt for bases and wearing courses.
| Analysis Of Bitumen 200-300 | ||||
| SPECIFICATION | Unti | Limit | TEST METHOD | |
| DENSITY @ 25 C | kg/m3 | 990-1040 | ASTM D70 or D3289 | |
| PENETRATION @ 25 C | Mm/10 | 200-300 | ASTM D5 | |
| SOFTENING POINT | C | 32 min | ASTM D36 | |
| DUCTILITY@ 25 C | Cm | 100 min | ASTM D 113 | |
| LOSS ON HEATING | wt% | 1 max | ASTM D6 | |
| DROP IN PENETERATION AFTER LOSS ON HEATING | % | 37 max | ASTM D5 | |
| FLASH POINT | C | 177 min | ASTM D92 | |
| SOLUBILITY IN TRICHLOROETHYLENE | wt% | 99.0 min | ASTM D2042 | |
| SPOT TEST | – | Negative | AASHTO T 102 | |
| VISCOSITY @ 60C | P | 200±50 | ASTM D2171 | |
| VISCOSITY @ 135C | Cst | 80 min | ASTM D1270 | |
| Test on Residue From Thin Film Oven Test (ASTM D1754) | ||||
| Retained penetration after (T.F.O.T) | % | 40 min | ASTM D5 | |
| Ductility . (25C), 5cm/min, cm after TFOT | cm | 100 | ASTM D113 | |
| VISCOSITY @ 60C | P | 1250 max | ASTM D2171 | |
Bitumen 20-30
Bitumen 20-30 which is obtained by performing aeration process on vacuum baton (raw material of bitumen production which is taken from the bottom of distillation tower in vacuum of oil refineries) in bitumen production units and degree of permeability (determination of stiffness) Bitumen) it should be between 20 and 30.
Bitumen 30-40
Bitumen 30-40 is bitumen that is obtained by performing an aeration process on vacuum baton (raw material for bitumen production which is taken from the bottom of the distillation tower in the vacuum of oil refineries) in bitumen production units and the degree of permeability (determination The hardness of bitumen) is between 30 and 40.
Bitumen 30-45
Bitumen 30-45, penetration 30 to 45 produced in this unit, which has a penetration of 30 to 45 bitumen and its softness is 52 to 60, is selected according to the needs of the project. Bitumen is a derivative of oil produced in an oil refinery. Bitumen is a substance that dissolves in carbon sulfide and carbon tetrachloride and is solid when exposed to ambient temperature. According to the needs of the project, by raising its temperature, it changes from a solid-state to a smooth paste state
Bitumen 10-20
Bitumen 10-20 is bitumen that is obtained by performing an aeration process on vacuum baton (raw material for bitumen production, which is taken from the bottom of the distillation tower in the vacuum of oil refineries) in bitumen production units and the degree of permeability (determination The hardness of bitumen) is between 10 and 20. The main common applications of this product are in the tropics and insulation and sound and shock absorption.
Bitumen 15-90
It is bitumen that is aerated by mixing two raw materials, vacuum baton and vacuum slab in bitumen production reactors under our special pressure and temperature between 200 to 300 degrees Celsius to combine the hydrogen atoms in the bitumen molecules with air oxygen and create Polymerization reactions yield heavier hydrocarbons that have a lower degree of penetration and a softer point than the original pure bitumen. This type of bitumen has a softness of 90 and a permeability of 15.
The application of this type of bitumen is mostly for covering the floor of water channels – cracks in concrete pavements – filling the joints of concrete surfaces – construction works – production of various types of waterproofing
Bitumen 35-50
Bitumen 35-50 is bitumen that is obtained by performing aeration process on vacuum baton (raw material of bitumen production which is taken from the bottom of distillation tower in the vacuum of oil refineries) in bitumen production units and degree of permeability The hardness of bitumen) is between 35 and 50.
Bitumen 40-50
Bitumen 40-50 is which is obtained by performing aeration process on vacuum baton (raw material of bitumen production which is taken from the bottom of distillation tower in the vacuum of oil refineries) in bitumen production units so that its permeability is between 40 Up to 50. Used in road construction industries for tropical areas, insulation and also the production of liquid bitumen is one of the applications of this type of bitumen
Bitumen 40-60
Bitumen 40-60 bitumen which is obtained by performing an aeration process on vacuum baton (raw material for bitumen production which is taken from the bottom of the distillation tower in the vacuum of oil refineries) in bitumen production units The hardness of bitumen) is between 40 and 60.
BITUMEN 50-60
Bitumen is 60-50 bitumen which is done by aeration process on vacuum baton (raw material of bitumen production which is taken from the bottom of distillation tower in the vacuum of oil refineries).
BITUMEN 60-90
The condition of refinery bitumen depends on its temperature. The relationship between temperature and hardness of different types of bitumen depends on the type of crude oil and its polishing method and the degree of permeability of bitumen 60-90 between 6 to 9 mm. Is the road. Are. Used for asphalt production and mainly used in hot asphalt production for surface coating. It is mostly used in various types of bitumen and is a necessary material for other bitumen products.
Bitumen 50-70
Bitumen is 50-70 bitumen which is done by aeration process on vacuum baton (raw material of bitumen production which is taken from the bottom of distillation tower in the vacuum of oil refineries).
Bitumen 70-100
He penetration bitumen 70-100 produced in this unit, which has 70-100 bitumen and its softness is 43 to 51, it is selected according to the needs of the project.
BITUMEN 80-100
Bitumen is a standard bitumen of penetration type, which is commonly known as road grade bitumen and has extraordinary properties for road construction and asphalt and road surface. This type of bitumen is mainly used in making hot asphalt mixtures. Penetration grade bitumens such as 80-100 bitumen are bitumens that are obtained by performing an aeration process on the bottom of the distillation tower, known as vacuum baton so that its degree of permeability is between 80 and 100. Infiltration grade bitumens have thermoplastic properties, this property causes the viscosity of bitumen to decrease at high temperatures and its viscosity to increase at low temperatures. Meanwhile, 80-100 bitumen is most used in the preparation of the road surfaces.
Bitumen 100-150
Bitumen 100-150, The penetration bitumen is 80 to 100 produced in this unit, which has a penetration of 150-100 and its softness is 39 to 47, is selected according to the needs of the project.
Bitumen 160-220
Bitumen 160-220 obtained by performing aeration process on vacuum baton (raw material for bitumen production taken from the bottom of distillation tower in the vacuum of oil refineries) in bitumen production units and degree of permeability (determination of stiffness) Bitumen) it should be between 220 and 160.
Bitumen 250-330
Bitumen 250-330 is obtained by performing aeration process on vacuum baton (raw material of bitumen production which is taken from the bottom of distillation tower in the vacuum of oil refineries) in bitumen production units and degree of permeability (determination The hardness of bitumen) is between 250 and 230.